美国亨斯迈物性表

查看报价 |

规格用途

规格级别		外观颜色
该料用途
备注说明

技术参数

性能项目		试验条件[状态]	测试方法	测试数据	数据单位
物理性能	比重2		ASTMD792	1.14	g/cm³
物理性能	密度3		DIN53478	1.14	g/cm³
物理性能	MeltVolume-FlowRate(MVR)(160°C/8.7kg)			35.0	cm³/10min
机械性能	Abrasion2	--	DIN53516	43	mm³
机械性能	Abrasion2	--	ASTMD395	43	mm³
ELASTOMERS	弹性体		TestMethod	NominalValue	Unit
ELASTOMERS	TensileSet3(200%Strain)		ASTMD412	8	%
ELASTOMERS	TensileSet3(200%Strain)		DIN53504	8	%
ELASTOMERS	TensileStress4(100%Strain,0.635mm)		ASTMD412	2.34	MPa
ELASTOMERS	TensileStress4(100%Strain,0.635mm)		DIN53504	1.40	MPa
ELASTOMERS	TensileStress4(300%Strain,0.635mm)		ASTMD412	4.07	MPa
ELASTOMERS	TensileStress4(300%Strain,0.635mm)		DIN53504	2.40	MPa
ELASTOMERS	TensileStrength4(Break,0.635mm)		ASTMD412	7.52	MPa
ELASTOMERS	TensileStress4(Break,0.635mm)		DIN53504	10.0	MPa
ELASTOMERS	TensileElongation4(Break,0.635mm)		ASTMD412	720	%
ELASTOMERS	TensileElongation4(Break,0.635mm)		DIN53504	900	%
ELASTOMERS	TearStrength4(0.635mm)		ASTMD624	35.9	kN/m
ELASTOMERS	TearStrength4(0.635mm)		DIN53515	25	kN/m
ELASTOMERS	压缩永久变形2	23°C,70hr	ASTMD395	40	%
ELASTOMERS	压缩永久变形2	70°C,24hr	ASTMD395	80	%
ELASTOMERS	压缩永久变形2	23°C,70hr	DIN53517	35	%
ELASTOMERS	压缩永久变形2	70°C,24hr	DIN53517	60	%
ELASTOMERS	巴肖氏弹性		ASTMD2632	60	%
硬度	肖氏硬度	邵氏A,注塑	ASTMD2240	56
硬度	肖氏硬度	邵氏D,注塑	ASTMD2240	15
硬度	肖氏硬度	邵氏A,注塑	DIN53505	55
硬度	肖氏硬度	邵氏D,注塑	DIN53505	15
热性能	熔融温度		InternalMethod	98.9to130	°C
热性能	TMA4	High:635.0µm	InternalMethod	145	°C
热性能	TMA4	Low:635.0µm	InternalMethod	110	°C

打印

【免责声明】

找塑料发布此信息目的在于方便用户查阅，对于所有的数据及建议等给用户带来的不确定因素和后果概不负责。因此，用户与使用者在使用此产品之前，应向生产商或采购商索取或确认数据的可靠性。

热门牌号: 1PP | K8003 | 燕山石化; 2ABS | 275 | 上海高桥; 3LDPE | 2426H | 大庆石化; 4PP | 6345 | BP; 5LLDPE | DFDA-7042 | 大庆石化; 6PP | K8009（PPB-M09） | 武汉石化; 7PP | 1102K | 神华宁煤; 8PP | 100-GA09 | BP

最近浏览

TPU-聚脂/IROGRAN® A 60 E 4902/美国亨斯迈 物性表

TPU-聚脂/IROGRAN® A 60 E 4902/美国亨斯迈物性表